新闻列表>技术文章---304不锈钢硬度，用途，不锈钢硬度抗拉强度对照表 |
技术文章---304不锈钢硬度，用途，不锈钢硬度抗拉强度对照表
| 文章来源：沃施莱格 发布作者：管理员 点击率：25048 发表时间：2012/11/20 14:49:17 |
|
|
|
|
304不锈钢硬度，用途，不锈钢硬度抗拉强度对照表 |
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 硬度，抗拉强度对照表 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
维氏(HV) |
洛氏HRC |
洛氏HRA |
强度N/mm2 |
|
维氏(HV)
|
洛氏RC |
洛氏RA |
强度N/mm2 |
|
维氏(HV)
|
洛氏RC |
洛氏RA |
强度N/mm2 |
|
|
625 |
57 |
79.5 |
2315 |
400 |
42 |
71.7 |
1350 |
260 |
26 |
63.3 |
895 |
|
|
605 |
56 |
78.9 |
2210 |
389 |
41 |
71.7 |
1310 |
254 |
25 |
62.8 |
875 |
|
|
587 |
55 |
78.4 |
2115 |
378 |
40 |
70.6 |
1275 |
247 |
24 |
62.3 |
845 |
|
|
569 |
54 |
77.9 |
2030 |
368 |
39 |
70.1 |
1235 |
241 |
23 |
61.7 |
825 |
|
|
551 |
53 |
77.4 |
1945 |
358 |
38 |
69.6 |
1200 |
235 |
22 |
61.2 |
805 |
|
|
535 |
52 |
76.9 |
1875 |
348 |
37 |
69 |
1170 |
229 |
21 |
60.7 |
790 |
|
|
520 |
51 |
76.3 |
1805 |
339 |
36 |
68.5 |
1140 |
224 |
20 |
60.2 |
770 |
|
|
504 |
50 |
75.8 |
1750 |
329 |
35 |
68 |
1115 |
218 |
19 |
59.7 |
755 |
|
|
489 |
49 |
75.3 |
1680 |
321 |
34 |
67.5 |
1085 |
213 |
18 |
59.1 |
739 |
|
|
475 |
48 |
74.8 |
1620 |
312 |
33 |
67 |
1060 |
208 |
17 |
58.6 |
724 |
|
|
461 |
47 |
74.2 |
1580 |
304 |
32 |
66.4 |
1030 |
203 |
16 |
58.1 |
710 |
|
|
443 |
46 |
73.7 |
1530 |
289 |
30 |
65.4 |
985 |
198 |
15 |
57.6 |
690 |
|
|
435 |
45 |
73.2 |
1480 |
281 |
29 |
64.9 |
950 |
193 |
14 |
57.1 |
677 |
|
|
423 |
44 |
72.7 |
1440 |
274 |
28 |
64.4 |
950 |
189 |
13 |
56.5 |
662 |
|
|
411 |
43 |
72.2 |
1390 |
267 |
27 |
62.8 |
915 |
180 |
11 |
55.5 |
625 |
|
|
|
| 名词解释：布氏硬度（HB），洛氏硬度（HR），维氏硬度（HV） |
|
|
|
| ⑴布氏硬度（HB） |
| 以一定的载荷（一般3000kg）把一定大小（直径一般为10mm）的淬硬钢球压入材料表面，保持一段时间，去载后，负荷与其压痕面积之比值，即为布氏硬度值（HB） |
，单位为公斤力/mm2
(N/mm2)。 |
| ⑵洛氏硬度（HR） |
| 当HB>450或者试样过小时，不能采用布氏硬度试验而改用洛氏硬度计量。它是用一个顶角120°的金刚石圆锥体或直径为1.59、3.18mm的钢球，在一定载荷下压 |
| 入被测材料表面，由压痕的深度求出材料的硬度。根据试验材料硬度的不同，分三种不同的标度来表示： |
| HRA：是采用60kg载荷和钻石锥压入器求得的硬度，用于硬度极高的材料（如硬质合金等）。 |
| HRB：是采用100kg载荷和直径1.58mm淬硬的钢球，求得的硬度，用于硬度较低的材料（如退火钢、铸铁等）。 |
| HRC：是采用150kg载荷和钻石锥压入器求得的硬度，用于硬度很高的材料（如淬火钢等）。 |
| ⑶维氏硬度（HV） |
以120kg以内的载荷和顶角为136°的金刚石方形锥压入器压入材料表面，用材料压痕凹坑的表面积除以载荷值，即为维氏硬度值（HV） |
|
304不锈钢硬度，用途，不锈钢硬度抗拉强度对照表 |
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 硬度，抗拉强度对照表 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
维氏(HV) |
洛氏HRC |
洛氏HRA |
强度N/mm2 |
|
维氏(HV)
|
洛氏RC |
洛氏RA |
强度N/mm2 |
|
维氏(HV)
|
洛氏RC |
洛氏RA |
强度N/mm2 |
|
|
625 |
57 |
79.5 |
2315 |
400 |
42 |
71.7 |
1350 |
260 |
26 |
63.3 |
895 |
|
|
605 |
56 |
78.9 |
2210 |
389 |
41 |
71.7 |
1310 |
254 |
25 |
62.8 |
875 |
|
|
587 |
55 |
78.4 |
2115 |
378 |
40 |
70.6 |
1275 |
247 |
24 |
62.3 |
845 |
|
|
569 |
54 |
77.9 |
2030 |
368 |
39 |
70.1 |
1235 |
241 |
23 |
61.7 |
825 |
|
|
551 |
53 |
77.4 |
1945 |
358 |
38 |
69.6 |
1200 |
235 |
22 |
61.2 |
805 |
|
|
535 |
52 |
76.9 |
1875 |
348 |
37 |
69 |
1170 |
229 |
21 |
60.7 |
790 |
|
|
520 |
51 |
76.3 |
1805 |
339 |
36 |
68.5 |
1140 |
224 |
20 |
60.2 |
770 |
|
|
504 |
50 |
75.8 |
1750 |
329 |
35 |
68 |
1115 |
218 |
19 |
59.7 |
755 |
|
|
489 |
49 |
75.3 |
1680 |
321 |
34 |
67.5 |
1085 |
213 |
18 |
59.1 |
739 |
|
|
475 |
48 |
74.8 |
1620 |
312 |
33 |
67 |
1060 |
208 |
17 |
58.6 |
724 |
|
|
461 |
47 |
74.2 |
1580 |
304 |
32 |
66.4 |
1030 |
203 |
16 |
58.1 |
710 |
|
|
443 |
46 |
73.7 |
1530 |
289 |
30 |
65.4 |
985 |
198 |
15 |
57.6 |
690 |
|
|
435 |
45 |
73.2 |
1480 |
281 |
29 |
64.9 |
950 |
193 |
14 |
57.1 |
677 |
|
|
423 |
44 |
72.7 |
1440 |
274 |
28 |
64.4 |
950 |
189 |
13 |
56.5 |
662 |
|
|
411 |
43 |
72.2 |
1390 |
267 |
27 |
62.8 |
915 |
180 |
11 |
55.5 |
625 |
|
|
|
| 名词解释：布氏硬度（HB），洛氏硬度（HR），维氏硬度（HV） |
|
|
|
| ⑴布氏硬度（HB） |
| 以一定的载荷（一般3000kg）把一定大小（直径一般为10mm）的淬硬钢球压入材料表面，保持一段时间，去载后，负荷与其压痕面积之比值，即为布氏硬度值（HB） |
，单位为公斤力/mm2
(N/mm2)。 |
| ⑵洛氏硬度（HR） |
| 当HB>450或者试样过小时，不能采用布氏硬度试验而改用洛氏硬度计量。它是用一个顶角120°的金刚石圆锥体或直径为1.59、3.18mm的钢球，在一定载荷下压 |
| 入被测材料表面，由压痕的深度求出材料的硬度。根据试验材料硬度的不同，分三种不同的标度来表示： |
| HRA：是采用60kg载荷和钻石锥压入器求得的硬度，用于硬度极高的材料（如硬质合金等）。 |
| HRB：是采用100kg载荷和直径1.58mm淬硬的钢球，求得的硬度，用于硬度较低的材料（如退火钢、铸铁等）。 |
| HRC：是采用150kg载荷和钻石锥压入器求得的硬度，用于硬度很高的材料（如淬火钢等）。 |
| ⑶维氏硬度（HV） |
以120kg以内的载荷和顶角为136°的金刚石方形锥压入器压入材料表面，用材料压痕凹坑的表面积除以载荷值，即为维氏硬度值（HV） |
| 名词解释：布氏硬度（HB），洛氏硬度（HR），维氏硬度（HV） |
|
|
|
| ⑴布氏硬度（HB） |
| 以一定的载荷（一般3000kg）把一定大小（直径一般为10mm）的淬硬钢球压入材料表面，保持一段时间，去载后，负荷与其压痕面积之比值，即为布氏硬度值（HB） |
，单位为公斤力/mm2
(N/mm2)。 |
| ⑵洛氏硬度（HR） |
| 当HB>450或者试样过小时，不能采用布氏硬度试验而改用洛氏硬度计量。它是用一个顶角120°的金刚石圆锥体或直径为1.59、3.18mm的钢球，在一定载荷下压 |
| 入被测材料表面，由压痕的深度求出材料的硬度。根据试验材料硬度的不同，分三种不同的标度来表示： |
| HRA：是采用60kg载荷和钻石锥压入器求得的硬度，用于硬度极高的材料（如硬质合金等）。 |
| HRB：是采用100kg载荷和直径1.58mm淬硬的钢球，求得的硬度，用于硬度较低的材料（如退火钢、铸铁等）。 |
| HRC：是采用150kg载荷和钻石锥压入器求得的硬度，用于硬度很高的材料（如淬火钢等）。 |
| ⑶维氏硬度（HV） |
以120kg以内的载荷和顶角为136°的金刚石方形锥压入器压入材料表面，用材料压痕凹坑的表面积除以载荷值，即为维氏硬度值（HV） | |
|
|
|
|
|
|
|
|
|
|
|
|